What Chemical Formula Do You Get When Mixing Copper & Aluminum?

Aluminum and copper can form the intermetallic compound CuAl2.
••• Comstock Images/Stockbyte/Getty Images

Copper and aluminum can be combined to form a copper-aluminum alloy. An alloy is a mixture, and therefore does not have a chemical formula. However, under very high temperature, copper and aluminum can form a solid solution. When this solution cools, the intermetallic compound CuAl2, or copper aluminide, can form as a precipitate.

Compounds and Alloys

A compound has a fixed ratio between its constituent elements. No matter how much of a compound you have, the ratio between the different atoms is the same. A mixture, on the other hand, can involve varying amounts of its constituent elements. A metal alloy is a mixture of two or more metals in any ratio. Therefore, an alloy does not have a chemical formula. Instead, alloys are described in terms of percentages. These percentages can change when more of one of the metals is added.

Solid Solution

When copper and aluminum are heated to 550 degrees Celsius (1,022 degrees Fahrenheit), solid copper will dissolve in the aluminum, forming a solution. At this temperature, the copper-aluminum solution can contain up to 5.6 percent copper by weight. This solution is saturated; it can hold no more copper. As a saturated copper-aluminum solution cools, the solubility of copper decreases and the solution becomes supersaturated. When the copper eventually precipitates out of solution, it forms the intermetallic compound CuAl2.

Intermetallic Compounds

The intermetallic compound CuAl2 forms slowly after the initial solution is created. Over time, copper atoms can move through the alloy due to diffusion. This movement leads to the formation of CuAl2 crystals. This compound always contains two aluminum atoms for every one copper atom; it is 49.5 percent aluminum by weight. Because of this fixed ratio, the compound has a definite chemical formula.

Precipitation Hardening

The particular orientation of the atoms in aluminum leads to slipping between planes of atoms. This translates to a reduced strength. When the CuAl2 crystals form, this slippage is lessened. This process is called precipitation hardening, and helps increase the strength of a copper-aluminum alloy. Manufacturers can regulate temperature over time to maximize this hardening.

Other Compounds of Copper and Aluminum

CuAl2 is the dominant intermetallic compound of copper and aluminum. However, the two metals can also form the intermetallic compounds CuAl and Cu9Al4. These compounds can form over time after the initial formation of CuAl2. The formation of these other compounds depends on the temperature, time and site of copper precipitation.

Related Articles

How to Find the Percent of Concentration of Copper...
How to Write the Net Ionic Equation for the Reaction...
Examples of Single Replacement Reactions
Why Do Pennies Corrode?
Different Types of Alloys & Use
What Chemicals Rust Metal Rapidly?
What Is ARCAP Alloy?
Do Metal Atoms Lose Their Valence Electrons When Forming...
Aluminum Hardness Classification
Can Brass Be Magnetized?
How to Find Heat Reaction When Zn Reacts With HCl
Type of Reactions With Copper & Nitric Acid
Causes of Gold Discoloration
Differences Between a Compound and a Solid Solution
Elements Found in Household Products
Physical and Chemical Properties for the Element Aluminum
What Is the Metallic Ion in the Compound CuCl2?
Why Do Hydrates Change Color When Heated?
Describe the Process of Electrolysis in the Production...

Dont Go!

We Have More Great Sciencing Articles!